Daido creates the next stage beyond what the customer “wants”
Product type: Synthetic resin solution
DAIKALAC
DAIKALAC is a solution type of synthetic resin obtained by the polymerization of monomers such as vinyl acetate, acrylic ester and styrene in the presence of a solvent such as ethyl acetate and methanol. Solvent-free powdered DAIKALAC, which is obtained by desolventizing after polymerization, is also available.
＜Optical applications＞
| DAIKALAC | Main features | Solvent | Non volatile content (%) |
Viscosity (mPa・s) |
Adhesive strength (N/25mm) |
Typical applications | Net weight Packaging |
|---|---|---|---|---|---|---|---|
| 5021 | Acid-free, excellent adhesion to glass | Ethyl acetate | 30 | 6,000 | 20 | Optically clear adhesive for touch panel, heat and humidity resistant and ITO corrosion resistant | 170kg Drum |
| 5022 | Acid-free, Excellent gap filling ability | Ethyl acetate | 30 | 4,000 | 13 | Optically clear adhesive for touch panel, heat and humidity resistant and ITO corrosion resistant | 170kg Drum |
| 5250 | Acid-free, human sebum resistant | Ethyl acetate | 40 | 14,000 | 20 | Optically clear adhesive for touch panel, heat and humidity resistant and ITO corrosion resistant | 170kg Drum |
*The above table shows typical values.
▲ To page top＜Industrial applications＞
| DAIKALAC | Main features | Solvent | Non volatile content (%) |
Viscosity (mPa・s) |
Adhesive strength (N/25mm) |
Typical applications | Net weight Packaging |
|---|---|---|---|---|---|---|---|
| 5040 | Acrylic copolymer | Toluene/Methanol | 40 | 5,500 | 12 | Industrial tape | 180kg Drum |
| R‐70 | Acrylic copolymer | Toluene/Ethyl acetate | 36 | 3,000 | 10 | Industrial tape | 180kg Drum |
| 5550B | Acrylic copolymer | IPA/toluene/Ethyl acetate | 70 | 8,000 | 18 | Thick film coating | 15kg Can |
*The above table shows typical values.
▲ To page topProduct type: Synthetic resin emulsion
VINYSOL
VINYSOL is an emulsion (polymer microparticles) obtained by the emulsion polymerization of monomers such as acrylic ester and vinyl acetate. Monomers can be selected to control glass transition temperature (Tg) to a desired level whereby allowing the use of VINYSOL in a variety of applications such as pressure-sensitive adhesives, paint and ink binders, and textile hard finishes.
＜Industrial applications＞
| VINYSOL | Main features | Non volatile content (%) |
Viscosity (mPa・s) |
pH | Adhesive strength (N/25mm) |
Typical applications | Net weight Packaging |
|---|---|---|---|---|---|---|---|
| 1091 | Acrylic copolymer | 40 | 2,400 | 8.3 | 0.2 | Masking | 200kg Drum |
| 1193 | Acrylic copolymer | 40 | 1,800 | 7.9 | 4 | Masking | 200kg Drum |
| 1094 | Acrylic copolymer | 44 | 2,400 | 7.8 | 2 | Masking | 200kg Drum |
| 1024 | Acrylic copolymer | 57 | 4,200 | 7.8 | 9 | Films | 1000kg Container |
| 1096 | Acrylic copolymer | 44 | 6,200 | 8.3 | 5 | Films | 200kg Drum |
*The above table shows typical values.