Daido creates the next stage beyond what the customer “wants”
Product type: Synthetic resin solution (UV-curable)
DAIOLET
DAIOLET is a coating material that cures when exposed to ultraviolet (UV) radiation. It delivers an ultra-hard coating compared to typical resins and is used in precision coatings for LCD televisions and touch panels that require films of high hardness.
| DAIOLET | Main features | Non volatile content (%) |
Viscosity (mPa・s) |
Main solvent | Hardness | Typical applications | Net weight Packaging |
|---|---|---|---|---|---|---|---|
| 5790C | Low-curl | 40 | 10 | MEK | 3H | UV hard coating, scratch resistance | 15kg Can |
| 5790HM | Water repellent | 40 | 10 | MEK | 3H | UV hard coating, for antifouling property | 15kg Can |
| 5820C | Good balance of hardness and Extensibility | 40 | 10 | MEK | 2H | UV hard coating, for processing and molding | 15kg Can |
| 5825K | Good balance of hardness and Extensibility | 40 | 10 | MEK | F | UV hard coating, for processing and molding | 15kg Can |
| 5848 | High refractive index | 40 | 10 | MEK | 2H | UV hard coating, for index matching coating | 15kg Can |
| 5790B | Solvent-free | 100 | 100 | ― | H－2H | UV hard coating, for imprinting | 16kg Can |
*The above table shows typical values.
▲ To page top| DAIOLET | Main features | Non volatile content (%) |
Viscosity (mPa・s) |
Main solvent | Adhesive strength (N/25mm) |
Typical applications | Net weight Packaging |
|---|---|---|---|---|---|---|---|
| 5960J | Resistant to whitening under heat and humidity | 100 | 7,000 | ― | 40 | UV pressure-sensitive adhesives, for optically clear adhesives | 15kg Can |
| 5960JM | Cured with a metal halide lamp | 100 | 7,000 | ― | 55 | UV pressure-sensitive adhesives, for optically clear adhesives | 15kg Can |
| 5952 | Two-stage curing | 40 | 4,500 | Ethyl acetate | 15 | UV pressure-sensitive adhesives, for optically clear adhesives | 15kg Can |
| 3877KE | Low curing shrinkage | 100 | 240 | ― | 12 | UV adhesives, for film lamination | 15kg Can |
*The above table shows typical values.
▲ To page top