Daido creates the next stage beyond what the customer “wants”
We affixed adhesive tape (50-μm adhesive layer) over a 10-μm height gradation caused by black ink and applied pressure over it with a 2-kg roller. After leaving it at 23ºC for 24 hours, we made visual observations.
| Product number | Features | Non-volatile content |
|---|---|---|
| DAIKALAC 5021 | Adhesion to glass (high adhesive strength) | 30％ |
| DAIKALAC 5022 | Adhesion to glass (high adhesive strength) | 30％ |
We affixed adhesive tape (50-μm adhesive layer) to a glass panel and applied pressure over it with a 2-kg roller. We then applied a sufficient amount of “artificial sebum solution (dyed red)” on the adhesive layer. After leaving it at 85ºC and 85% RH for 48 hours, we made visual observations.
Synthetic sebum solution: Formulation of triglyceride, isostearic acid and squalane
| Product number | Features | Non-volatile content |
|---|---|---|
| P-7239A | High solid content (Composition of DAIKALAC 5021) | 60％ |
| DAIKALAC 5250 | Human sebum resistant | 40％ |
We affixed adhesive tape (50-μm adhesive layer) to MR58 sheets (PC/PMMA by Mitsubishi Gas Chemical) and applied pressure over it with a 2-kg roller. After leaving them at 23ºC for 24 hours, then one at 85ºC and dry conditions and the other at 60ºC, 95% RH for 240 hours, we made visual observations.
| Product number | Features | Non-volatile content |
|---|---|---|
| P-7240M | Adding resistance to foaming under heat and humidity to plastic panels | 40％ |
| P-7240N | Adding resistance to foaming under heat and humidity to plastic panels | 40％ |